ACEROS PARA BAJA TEMPERATURA
Aceros formulados para conservar tenacidad y resistencia al impacto en condiciones criogénicas o de muy baja temperatura. Utilizados en gas, energía y almacenamiento criogénico.
ACERO ASTM A350 LF2
ACERO ASTM A333 GR.3
ACERO ASTM A420 WPL3
ACERO ASTM A333 GR.6
ACERO ASTM A420 WPL6
Composición química de ACEROS PARA BAJA TEMPERATURA
ACERO ASTM A350 LF2
C: ≤ 0.3%
Si: 0.15% ~ 0.3%
P: ≤ 0.035%
S: ≤ 0.04%
V: ≤ 0.08%
Cr: ≤ 0.3%
Mn: 0.6% ~ 1.35%
Ni: ≤ 0.4%
Cu: ≤ 0.4%
Mo: ≤ 0.12%
Fe
97.125%
Fe: balance · 97.125%
C
Si
P
S
V
Cr
Mn
Ni
Cu
Mo
Ver composición
- C C: ≤ 0.3%
- Si Si: 0.15% ~ 0.3%
- P P: ≤ 0.035%
- S S: ≤ 0.04%
- V V: ≤ 0.08%
- Cr Cr: ≤ 0.3%
- Mn Mn: 0.6% ~ 1.35%
- Ni Ni: ≤ 0.4%
- Cu Cu: ≤ 0.4%
- Mo Mo: ≤ 0.12%
- Fe Fe: balance · 97.125%
ACERO ASTM A333 GR.3
C: ≤ 0.19%
Si: ≤ 0.1%
P: ≤ 0.025%
S: ≤ 0.025%
V: ≤ 0.08%
Cr: ≤ 0.15%
Mn: 0.31% ~ 0.64%
Ni
3.5%
Ni: 3.18% ~ 3.82%
Cu: ≤ 0.4%
Mo: ≤ 0.12%
Fe
94.935%
Fe: balance · 94.935%
C
Si
P
S
V
Cr
Mn
Cu
Mo
Ver composición
- C C: ≤ 0.19%
- Si Si: ≤ 0.1%
- P P: ≤ 0.025%
- S S: ≤ 0.025%
- V V: ≤ 0.08%
- Cr Cr: ≤ 0.15%
- Mn Mn: 0.31% ~ 0.64%
- Ni Ni: 3.18% ~ 3.82%
- Cu Cu: ≤ 0.4%
- Mo Mo: ≤ 0.12%
- Fe Fe: balance · 94.935%
ACERO ASTM A420 WPL3
C: ≤ 0.19%
Si: ≤ 0.1%
P: ≤ 0.025%
S: ≤ 0.025%
Mn: 0.31% ~ 0.64%
Ni
3.5%
Ni: 3.18% ~ 3.82%
Fe
95.685%
Fe: balance · 95.685%
C
Si
P
S
Mn
Ver composición
- C C: ≤ 0.19%
- Si Si: ≤ 0.1%
- P P: ≤ 0.025%
- S S: ≤ 0.025%
- Mn Mn: 0.31% ~ 0.64%
- Ni Ni: 3.18% ~ 3.82%
- Fe Fe: balance · 95.685%
ACERO ASTM A333 GR.6
C: ≤ 0.3%
Si: ≤ 0.1%
P: ≤ 0.025%
S: ≤ 0.025%
Mn: 0.29% ~ 1.06%
Fe
98.875%
Fe: balance · 98.875%
C
Si
P
S
Mn
Ver composición
- C C: ≤ 0.3%
- Si Si: ≤ 0.1%
- P P: ≤ 0.025%
- S S: ≤ 0.025%
- Mn Mn: 0.29% ~ 1.06%
- Fe Fe: balance · 98.875%
ACERO ASTM A420 WPL6
C: ≤ 0.3%
Si: ≤ 0.1%
P: ≤ 0.025%
S: ≤ 0.025%
Mn: 0.29% ~ 1.06%
Fe
98.875%
Fe: balance · 98.875%
C
Si
P
S
Mn
Ver composición
- C C: ≤ 0.3%
- Si Si: ≤ 0.1%
- P P: ≤ 0.025%
- S S: ≤ 0.025%
- Mn Mn: 0.29% ~ 1.06%
- Fe Fe: balance · 98.875%